  • Investigation of Interlaminar Fracture Surfaces in Graphite/Epoxy Composite Material under Mixed-Mode Deformations
  • Sung Ho Yoon, Chang Sun Hong
  • 탄소섬유강화 복합재료의 혼합모우드 층간파단면 고찰
  • 윤성호, 홍창선
Abstract
In this study, interlaminar fracture toughness of graphite/epoxy composite material under mixed mode deformations was evaluated experimentally and fracture surfaces were investigated to obtain information on interlaminar fracture mechanism by means of a scanning electron microscope. An antisymmetric test fixture with interlaminar cracked specimen was employed. By rotating the loading angles, interlaminar fracture under mixed mode deformations was produced in which the direction of crack propagation and loading state at fracture were well defined. Morphology of fracture surfaces was sensitive to applied loading condition and provided an insight to estimate the state of stress at fracture.

본 연구에서는 탄소섬유강화 복합재료의 혼합모우드 층간파괴인성을 실험적인 방법에 의해 평가하였으며 층간파괴 메카니즘에 관한 정보를 얻기 위해 전자현미경을 통한 파단면 양상을 조사하였다. 층간균열 시편이 부착된 비대칭 형상의 실험장치는 하중각도에 따른 다양한 혼합모우드 변형을 유발시키며 균열진전 방향과 파괴가 발생하였을 때의 하중상태를 잘 정의할 수 있는 층간파괴를 제공해 주기 때문에 작용된 하중상태에 따른 파단면 양상의 조사가 가능하였다. 관찰된 탄소섬유강화 복합재료의 층간파단면 양상은 작용된 하중상태에 따라 민감하게 변하며 파괴가 발생하였을 때의 응력상태를 예측할 수 있는 좋은 정보를 제공하여 주었다.

Keywords:

This Article

  • 1988; 1(1): 1-9

    Published on Feb 28, 1988

Correspondence to

  • E-mail: