  • Calcination Condition of CsPbBr3-SiO2 Composite Nanoparticles
  • Min-Gi Jeon*, Rezaul MD Kabir*, Artavazd Kirakosyan*, Jihoon Choi*†

  • * Department of Materials Science and Engineering, Chungnam National University

  • CsPbBr3-SiO2 복합 나노입자의 소결 조건 연구
  • 전민기*· 레자울 카비르*· 알타바즈 키라코시안*· 최지훈*†

  • This article is an open access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/by-nc/4.0) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Owing to the superior optoelectronic properties, halide perovskites have emerged as next-generation materials for display application. In this study, we reported a novel route for CsPbBr3 calcination into porous SiO2 nanoparticles to overcome the stability issues of halide perovskite via a spatial confinement of crystal growth within SiO2 pores. The resulting CsPbBr3-SiO2 nanoparticles exhibited the photoluminescence (PL) emission peak at 515 nm under optimal calcination condition. In several polar solvents, PL properties of CsPbBr3-SiO2 nanoparticles was maintained owing to the enclosed pores during calcination process, suggesting their promising application for display color conversion film.


할라이드 페로브스카이트 물질은 우수한 광전특성으로 인해 차세대 디스플레이에 응용시킬 물질로서 주목받고 있다. 본 연구에서는 다공성 SiO2 나노입자의 기공 내부에서 제한시킨 결정 성장을 통하여 할라이드 페로브스카이트의 안정성 문제를 해결한, CsPbBr3의 새로운 소결법을 제안한다. 최적의 소결 조건에서 소결된 CsPbBr3-SiO2 나노입자는 515 nm의 발광 피크를 나타낸다. CsPbBr3-SiO2 나노입자는 소결 과정 중 닫힌 기공에 말미암아 몇 종의 극성 용매 속에서도 안정적으로 발광 특성을 유지할 수 있었으며, 이는 디스플레이용 색변환 필름으로서의 응용 가능성을 보여준다


Keywords: 할라이드 페로브스카이트(Halide perovskite), 템플릿 캡슐화(Template capsulation), 산화규소(SiO2), 다공성 나노입자(Porous nanoparticle)