The electrical contact resistance between the bipolar plate (BP) and the carbon felt electrode (CFE), which are in contact by the stack clamping pressure, has a great impact on the stack efficiency because of the relatively low clamping pressure of the vanadium redox flow battery (VRFB) stack. In this study, a polyethylene (PE) composite-CFE hybrid bipolar plate structure is developed through a local heat welding process to reduce such contact resistance and improve cell performance. The PE matrix of the carbon fiber composite BP is locally melted to create a direct contact structure between the carbon fibers of CFE and the carbon fibers of BP, thereby reducing the electrical contact resistance. Area specific resistance (ASR) and gas permeability are measured to evaluate the performance of the PE composite-CFE hybrid bipolar plate. In addition, an acid aging test is performed to measure stack reliability. Finally, a VFRB unit cell charge/discharge test is performed to compare and analyze the performance of the developed PE composite-CFE hybrid BP and the conventional BP

스택 체결압에 의해 접촉되는 분리판(BP)과 탄소펠트전극(CFE) 사이의 전기적 접촉저항은 상대적으로 낮은 바나듐 레독스 흐름전지(VRFB) 스택의 체결압 때문에 스택 효율에 큰 여향을 미친다. 본 연구에서는 이러한 접촉저항을 줄이고 셀 성능을 향상시키기 위해 국부 가열 접합 공정을 통해 폴리에틸렌(PE) 복합재료-CFE 하이브리드 BP 구조를 개발하였다. 탄소섬유 복합재료 BP의 PE 매트릭스를 국부적으로 녹여 CFE의 탄소 섬유와 BP의 탄소 섬유의 직접 접촉 구조를 만들어 전기 접촉 저항을 감소시겼다. PE 복합재료-CFE 하이브리드 BP의 성능을 평가하기 위해 면적비저항(ASR)과 기체투과도를 측정하였다. 또한 스택 신뢰성을 측정하기 위해 내산성 시험을 수행하였다. 최종적으로, 개발된 PE 복합재료-CFE 하이브리드 BP와 기존의 BP의 성능을 비교 분석하기 위하여 VFRB 단위셀 충/방전 시험을 수행하였다

Keywords: 열가소성(Thermoplastic), 탄소 펠트(Carbon felt), 분리판(Bipolar plate), 바나듐 레독스 흐름전지(Vanadium redox flow battery)