  • Mechanical and Thermal Properties of Phenolic Composite reinforced with Hybrid of Carbon Fabrics
  • Jae-Hong Kim*, Jong-Kyu Park**, Kyung-Ho Jung***, Tae-Jin Kang*+
  • 하이브리드화에 의한 탄소 직물 복합재료의 역학적 특성 및 열적 특성
  • 김재흥(서울대학교), 박종규(국방과학연구소), 정경호(삼성전자), 강태진(서울대학교)
Abstract
The mechanical and thermal properties of PAN-based/rayon-based carbon fabrics interply hybrid composite materials have been studied. Mechanical properties including tensile and interlaminar shear strengths were improved with increasing amount of continuous PAN-based carbon fabrics. The erosion rate and insulation index were determined through the torch test. Continuous rayon-based carbon fabrics composite indicated relatively low ablation resistant property. The thermal conductivity of hybrid composite of spun PAN-based/continuous rayon-based carbon fabrics is lower than that of the continuous PAN-based carbon fabrics composite.

본 연구에서는 전구체의 종류에 따라 PAN계/rayon계, 직물의 형태에 따라 연속사 및 방적사 탄소 직물을 사용하여 하이브리드 복합재료를 제조하여 역학적 특성과 열적 특성을 살펴보았다. 인장, 층간 전단강도 실험을 통해 연속사 PAN계 탄소 직물을 많이 사용한 하이브리드 복합재료에서 우수한 역학적 특성을 보이는 것으로 확인되었다. 토치 테스트에서는 rayon계 탄소 직물 복합재료의 삭마 저항성이 가장 떨어짐을 확인할 수 있었다. 또한, 방적사 PAN계 탄소 직물과 rayon계 탄소 직물을 하이브리드화한 복합재료가 면내 방향과 수직 방향 모두에서 저 열전도도 구현에 유리한 특성을 보여주었다.

Keywords: Carbon Fiber, Hybrid Composites, Ablation Property, Thermal Conductivity