  • Mixed-mode fracture toughness measurement of a composite/metal interface
  • Won-Seock Kim*, Chang-Jae Jang**, Jung-Ju Lee**+
  • 복합재료/금속 접착 계면의 혼합모드 파괴인성 측정
  • 김원석(한국항공우주연구원 위성구조팀), 장창재(한국과학기술원 기계공학과 대학원), 이정주(한국과학기술원 기계공학과)
Abstract
Interfacial fracture toughness under various mixed-mode loading is measured to provide a mixed-mode fracture criterion of a composite/metal bonded joint. Experimental fracture characterization tests were carried out using a SLB (single leg bending) specimen, which controls mode ratio with the specimen thickness. The experimental result of the SLB test conforms that interfacial fracture toughness increases as the mode II component increases. The effect of loading mode on interfacial crack growth is investigated on the basis of crack path observation using microscopic image acquisition technique. The influence of interfacial roughness on adhesion strength is also discussed.

복합재료/금속 접착 조인트의 파손기준을 제시하기 위하여 다양한 혼합모드 하중상태에서 계면파괴인성을 측정하였다. 계면파괴인성은 SLB 시편을 이용하여 측정하였으며 시편의 두께를 변화시킴으로 모드 혼합비율을 다양하게 설정하였다. 실험결과 계면의 파괴인성은 균열 열림에 비해 균열 미끄러짐 모드의 비율이 높은 하중상태에서 더 큰 값을 나타내었다. 균열 열림 및 미끄러짐 하중모드에 따른 계면파괴 거동의 차이를 균열진전 과정을 관찰한 현미경 영상을 기초로 고찰하였다. 표면거칠기가 접착 강도에 미치는 영향 또한 고찰되었다.

Keywords: adhesive bonding, interface, fracture toughness, mixed-mode

Keywords: 접착 결합, 계면, 파괴인성, 혼합모드