Original Article
  • Fatigue Characterization of Glass/Polypropylene Composite Bone Plates Locked with an Artificial Tibia under Moisture Environment
  • Min-Gu Han*, Seung-Hwan Chang**†
  • * 중앙대학교 기계공학부 **† 중앙대학교 기계공학부, Corresponding author (E-mail: phigs4@cau.ac.kr)
  • 인조골에 체결된 유리섬유/폴리프로필렌 복합재료 고정판의 수분 환경 피로 특성
  • 한민구* , 장승환**†
Abstract
ABSTRACT: In this study, bone plate made of glass/polypropylene composite material which was applied to an artificial bone was tested to check the service ability under fatigue loading. To check serviceability of composite bone plates fatigue test was carried out considering changes in the moisture absorption rate, locking position of screws and loading condition. Test results showed that all the tested specimens had the fatigue life more than one million cycles which was much higher fatigue life than the expected value of 650,000 cycles. Screw position was not critical impact on the deformation of the fracture site. In this paper, the mechanical performance of the glass/polypropylene composite was verified by fatigue test under various water absorption conditions, and this result may give useful information on the design of composite bone plate.

초 록: 본 연구에서는 유리섬유/폴리프로필렌 복합재료 고정판을 인조골에 체결하여 실제 골절치료 시술 상황을 모사하였으며, 고정판의 적합성을 판단하기 위하여 수분 흡수율, 스크류의 체결 상태, 하중 조건의 변화에 따른 피로 실험을 진행하였다. 실험 결과 0~12주 동안 수분 흡수가 이루어진 모든 시편에서 기대 수명인 65만 사이클 을 넘는 100만 사이클 이상의 피로 수명을 가짐을 확인하였다. 스크류 체결 상태는 골절부의 변형률 차이에 주목 할만한 영향을 미치지 못하였다. 본 논문에서는 유리섬유/폴리프로필렌 복합재료 고정판을 다양한 환경조건 하에 서 압축-압축 피로실험을 수행하여 기계적 우수성을 입증하였으며, 이 결과는 향후 금속 고정판을 복합재료 고정 판으로 대체하기 위한 관련 연구에 유용한 정보를 제공할 것으로 기대된다.

Keywords: glass/polypropylene composites, fatigue test, bone plate, water absorption

Keywords: 유리섬유/폴리프로필렌 복합재료, 피로 실험, 고정판, 수분 흡수