  • A Study on the Mechanical Properties of Braid Composites for the Manufacture of Aircraft Stringer
  • Jong Hyun Eun, Joon Suck Lee, Seung Hwan Park, Dong Hyun Kim, Jin Sung Chon, Ho Wook Yoo
  • Department of Fiber System Engineering, Yeungnam University, Gyeongsan 38541, Korea, Department of Composite Materials R&D Center, Textile for Life (T4L), Gyeongsan 38474, Korea
  • 항공기용 스트링거 제작을 위한 브레이드 복합재료의 물성에 관한 연구
  • 은종현, 이준석, 박승환, 김동현, 천진성, 유호욱
Abstract
In this paper, we have studied the physical properties of braided composites for use as aircraft stringers. Process variables such as drum winder speed, braid velocity, and mandrel diameter for 30°, 45° and 60° braid preforms were quantified and different epoxy resin types were applied to the braided preform using TGDDM, YD- 128. Physical properties such as tensile strength and flexural strength of braided composites were investigated. Thermal properties and decomposition temperature of epoxy resin were investigated by TGA analysis. As a result, the lower the angle of the braid composites, the higher the tensile strength and the Flexural strength. The physical properties of braided composites fabricated using TGDDM epoxy resin were superior to the physical properties of braided composites fabricated using YD-128 epoxy resin. This is because the molecular weight of TGDDM epoxy resin was higher than that of YD-128 epoxy resin.

본 논문에서는 항공기용 스트링거(Stringer)로 사용하기 위한 브레이드 복합재료(Braided composites)의 물성에 대해 연구하였다. 브레이드 프리폼(braid preform)을 30°, 45°, 60°로 제작하기 위해 드럼 와인더 속도, 브레이드 속도, 멘드럴 직경과 같은 공정변수들을 정량화시켰고, 에폭시 수지 종류를 TGDDM, YD-128로 브레이드 프리폼에 다르게 적용하여 각도에 따른 브레이드 복합재료의 인장강도, 굽힘강도를 섬유부피분율에 따라 규명하였으며, TGA 분석으로 열적 특성과 에폭시 수지의 분해 온도를 조사하였다. 그 결과 브레이드 프리폼의 각도가 낮을수록 인장강도와 굽힘강도가 향상됨을 확인하였고, 분자량이 높은 에폭시 수지를 사용할 때 물리적 성질이 향상되었다.

Keywords: Carbon fiber, Composite materials, Braid, Epoxy, Compression molding

Keywords: 탄소섬유, 복합재료, 브레이드, 에폭시, 압축성형