Original Article
  • Development of the CFRP Automobile Parts Using the Joint Structure of the Dissimilar Material
  • Kwan Ho Ko, Min Gu Lee, Mongyoung Huh
  • Composites Processing Division, Korea Institute of Carbon Convergence Technology, Jeonju 54853, Korea
  • 결합부 강화구조용 탄소복합재 자동차 부품 개발
  • 고관호, 이민구, 허몽영
Abstract
In this study, the development purpose is to replace steel Tie Rod of commercial vehicle to the carbon composite by a braiding process. CFRP tie rod was designed to meet the performance requirements of existing products by designing the cross section of the core for braiding weaving and the structural design of the joint between the core and the carbon fiber. The specimens were fabricated by braiding method and applied to structural analysis through test evaluation. The manufacturing process proceeded from braiding to infusion through post-curing process. The test evaluation of the final product was satisfactorily carried out by sequentially performing tensile test, torsion test, compression test and fatigue test. In addition, the weight of CFRP tie rod could be reduced by about 37% compared to existing products.

본 연구에서는 기존의 스틸재 타이로드를 브레이딩 공법을 적용한 탄소복합재로 개발하고자 하였다. 탄소복합재 타이로드는 기존 제품과 동등한 성능을 만족시키기 위하여 브레이딩 직조에 필요한 코어 단면설계, 코어와 탄소섬유의 접합부에 대한 구조형상설계를 진행하였다. 그리고 브레이딩 공법을 적용한 시편을 제작하여 시험평가를 통해 구조해석에 적용하였다. 제작 공정은 브레이딩 직조 후 인퓨전 공정을 거쳐 후경화 공정까지 진행하였으며 최종 제품에 대한 시험평가는 인장 시험, 비틀림 시험, 압축 시험과 피로시험을 순차적으로 진행하여 모두 만족시켰다. 또한 탄소복합재 타이로드의 중량을 기존 제품 대비 약 37% 정도 경량화시킬 수 있었다.

Keywords: CFRP, Braiding process, Tie rod, Composite design, Lightweight, Structural analysis

Keywords: 탄소섬유복합재, 브레이딩 공법, 타이 로드, 복합재 설계, 경량화, 구조해석

This Article

  • 2018; 31(6): 392-397

    Published on Dec 31, 2018